Abstract
<jats:p>The article is devoted to the synthesis and study of nitrogen-modified adsorbents. The adsorbents were synthesized from walnut shells by pyrolysis in a stream of water vapor with and without the introduction of ammonia into the reaction zone. The aim of the study was to establish the influence of the process temperature (650–750 °C) and gaseous ammonia on the structure and properties of nitrogen-modified carbon adsorbents. Low-temperature nitrogen adsorption, elemental analysis, and Fourier transform IR spectroscopy were used to study the composition and structure. It was found that increasing the pyrolysis temperature from 650 to 750 °C leads to an increase in the specific surface area from 396 to 777 m²/g and pore volume from 0.23 to 0.46 cm³/g. Modification with ammonia increases the nitrogen content to 3.1% (750 °C, 300 ml/h). IR spectra confirm the formation of C–N and C=N bonds on the carbon surface of the adsorbents.</jats:p> <jats:p>Статья посвящена синтезу и исследованию азот-модифицированных адсорбентов. Адсорбенты синтезировали из скорлупы грецкого ореха методом пиролиза в потоке водяного пара с и без ввода аммиака в реакционную зону. Цель работы — установить влияние температуры процесса (650–750 °C) и газообразного аммиака, на структуру и свойства углеродных адсорбентов. Для исследования состава и структуры использовали низкотемпературную адсорбцию азота, элементный анализ, ИК-Фурье спектроскопию. Найдено, что повышение температуры пиролиза с 650 до 750 °C приводит к росту удельной поверхности с 396 до 777 м²/г и объема пор с 0,23 до 0,46 см³/г. Модификация аммиаком увеличивает содержание азота до 3,1% (750 °C, 300 мл/ч). ИК-спектры подтверждают образование C–N и C=N связей на углеродной поверхности адсорбентов.</jats:p>